TRIDENT direct-drive materials experiments, Jan 2003 ("Guinness")

Tom Tierney, Damian Swift, and Bruce Remington
IM#

Objectives

Samples

Configuration

Normal configuration for Trident materials experiments. Optical spectrometry coupled into VISAR axis.

Fresnel zone plate for 5 mm drive; hex zone plate for 0.6 mm drive.

Shot log

Shot Target Drive VISAR Optical Pyrometer Comments
Material Thickness (um) Dia (mm) Pulse length (ns) Energy Scope Delay (ns) Sweep (ns) Delay (ns) Sweep (ns) Delay (ns) Spectro slit (um) CWL (nm) Filters Streak slit
1/15/2003
15375 Ta 60 5 2.4 134.1 209.0 50 2890 N/A N/A N/A N/A N/A N/A no trigger to Visar probe
15376 Ta 60 5 2.4 122.0 220.0 50 2890 N/A N/A N/A N/A N/A N/A *master delay 2915ns for scopes
1/16/2003
15378 Ta 30 5 2.4 111.0 220.0 20 2925 N/A N/A N/A N/A N/A N/A
15379 Ta 30 5 2.4 13.4 222.0 20 2927 N/A N/A N/A N/A N/A N/A amps 7,8,9 did not fire
15380 Ta 29 5 2.4 190.2 221.5 20 2927 N/A N/A N/A N/A N/A N/A
15381 Ta 30, 59 5 2.4 73.2 221.5 20 2927 N/A N/A N/A N/A N/A N/A VISAR unstable due to strong temperature variations in room.
15382 Ta 60 5 2.4 70.7 221.5 50 2890 N/A N/A N/A N/A N/A N/A
15383 Ta 29, 61 5 2.4 185.4 221.5 50 2890 N/A N/A N/A N/A N/A N/A
15384 Ta 28, 59 5 2.4 0.0 221.5 20 2930 N/A N/A N/A N/A N/A N/A
1/21/2003
15390 Fe 44, 23 5 2.4 215.0 221.5 50 2890 N/A N/A N/A N/A N/A N/A ** due to filter before calorimeter."Corr. Drive Energy" is correct.
15391 Fe 44, 23 5 2.4 210.0 221.5 50 2890 N/A N/A N/A N/A N/A N/A
15392 Fe 23 5 2.4 102.0 221.5 20 2928 N/A N/A N/A N/A N/A N/A
15393 Fe 23 5 2.4 29.0 221.5 20 2928 N/A N/A N/A N/A N/A N/A
15394 Fe 23 5 2.4 64.0 221.5 20 2928 N/A N/A N/A N/A N/A N/A
15395 Fe 22 5 2.4 144.0 221.5 20 2928 N/A N/A N/A N/A N/A N/A
15396 Fe 23 5 2.4 193.0 221.5 20 2928 N/A N/A N/A N/A N/A N/A
15397 Fe 40 5 2.4 198.0 221.5 20 2928 N/A N/A N/A N/A N/A N/A Fe+red epoxy+1000A Al + LiF window; delay not adjusted.
1/22/2003
15399 Fe 41, 24 5 2.4 154.0 221.5 50 2890 N/A N/A N/A N/A N/A N/A
15400 Fe 39, 21 5 2.4 214.0 221.5 50 2890 50 2890 100 750 OG550, NF 200 stacked targets adjustment. First shot with optical pyrometer setup
15401 Fe 39, 23 5 2.4 110.0 221.5 50 2895 50 2876 100 750 OG550 200 ** Pyro timing set using VISAR timing fiducial. Fiber broken, recleaved.
15402 Fe 39, 23 5 2.4 93.0 221.5 50 2895 50 2876 100 750 OG550 200
1/23/2003
15404 NiAl 100-02-6: 228; 110-02-8: 228 5 2.4 8.0 221.5 50 2930 50 2876 100 750 OG550 200 No crystal orientation relative to target normal
15405 NiAl 110-02-9: 266; 100-02-4: 267 5 2.4 5->7 221.5 50 2935 50 2876 100 750 OG550 200
15406 NiAl 111-02-5: 396 5 2.4 6.0 221.5 50 2955 50 2876 100 750 OG550 200
15407 NiAl 111-02-8: 543; 111-02-7: 563 5 2.4 23.0 221.5 50 2955 50 2876 100 750 OG550 200
15408 NiAl 111-02-10: 586; 111-02-11: 573 5 2.4 68.0 221.5 50 2960 50 2876 100 750 OG550 200 Targets shattered: did best possible on recovery
15409 NiAl 110-02-4: 309; 111-02-1: 370 5 2.4 11.0 221.5 50 2920 50 2918 100 750 OG550 200
15410 Ta 63, 28 5 2.4 124.0 221.5 50 2890 50 2888 100 750 OG550 200 Possible plasma light recorded on Pyrometer
15411 Ta 75, 30 5 2.4 63.0 221.5 50 2895 50 2893 100 750 OG550 200
15412 Ta 32, 75 5 2.4 24.0 221.5 20 2936 20 2934 100 750 OG550 200
15413 Fe 29, 37 5 2.4 32.0 221.5 20 2928 20 2926 100 750 OG550 200 ~50-micron gap between samples
1/26/2003
15415 Fe 39, 29 5 2.4 225.0 221.5 20 2928 20 2926 100 750 OG550 200 Line radiation recorded.
15416 Fe 38, 28 5 2.4 82.0 221.5 20 2928 20 2926 100 750 OG550 200
15417 Fe 38, 28 5 2.4 0.0 221.5 20 2928 20 2926 100 750 OG550 200
15418 NiTi 98 5 2.4 8.0 221.5 50 2905 50 2903 100 750 OG550 200 OD 0.9 in path of VISAR (weak, but tracable signals)
15419 NiTi 205 5 2.4 13.0 221.5 50 2927 50 2925 100 750 OG550 200
15420 Cal N/A 5 2.4 6.2 221.5 N/A N/A N/A N/A N/A N/A N/A N/A Low Energy photocalorimeter Calibrations
15421 Cal N/A 5 2.4 4.6 221.5 N/A N/A N/A N/A N/A N/A N/A N/A See Sheets "EnergyCal" and "CalRecord"
15422 Cal N/A 5 2.4 4.5 221.5 N/A N/A N/A N/A N/A N/A N/A N/A Result highmeter (in J) = 0.0344*lowmeter(in uJ)
15423 Cal N/A 5 2.4 5.9 221.5 N/A N/A N/A N/A N/A N/A N/A N/A
15424 Cal N/A 5 2.4 3.1 221.5 N/A N/A N/A N/A N/A N/A N/A N/A
15425 NiTi 104 5 2.4 6.0 221.5 50 2927 50 2925 100 750 OG550 200
15426 NiTi 207 5 2.4 4.6 221.5 50 2927 50 2925 100 750 OG550 200
1/27/2003
15428 NiTi 104 5 1.2 3.1 221.5 50 2905 N/A N/A N/A N/A N/A N/A
15429 NiTi 208 5 1.2 3.3 221.5 50 2927 N/A N/A N/A N/A N/A N/A
15430 NiTi 108 5 0.7 0.8 221.5 50 2905 N/A N/A N/A N/A N/A N/A
15431 NiTi 199 5 0.7 0.9 221.5 50 2927 N/A N/A N/A N/A N/A N/A
15432 NiTi 107 5 0.35 0.4 221.5 50 2905 N/A N/A N/A N/A N/A N/A * Had Abort
15433 NiTi 207 5 0.35 0.4 221.5 50 2927 N/A N/A N/A N/A N/A N/A
15434 NiTi 202 5 2.4 20.0 221.5 50 2927 N/A N/A N/A N/A N/A N/A
15435 NiAl B7 248 5 2.4 31.0 221.5 50 2920 N/A N/A N/A N/A N/A N/A ** Alignment challenge
15436 NiAl B1 346 5 2.4 10.9 221.5 50 2940 N/A N/A N/A N/A N/A N/A ** Swapped out #3 since marks not recognizable.
1/2x/2003
15438 NiAl B4 104 5 2.4 37.0^ 221.5 50 2892 N/A N/A N/A N/A N/A N/A ^ Corrected Energy here refers to filtered 2-w monitor
15439 NiAl 100-02-8: 300; 111-02-4: 385 5 2.4 20.0^ 221.5 50 2927 N/A N/A N/A N/A N/A N/A ^ raw is calc from low energy monitor.
15440 NiAl 100-02-12: 316; 111-02-2?: 437 5 2.4 7.1 221.5 50 2935 N/A N/A N/A N/A N/A N/A Step towards VISAR
15441 NiAl 100-02-9: 316; 111-02-3: 438 5 2.4 9.7 221.5 50 2935 N/A N/A N/A N/A N/A N/A Step towards VISAR
15442 NiAl B3 186 5 2.4 7.7 221.5 50 2910 N/A N/A N/A N/A N/A N/A Step towards Drive
15443 Al 30 0.6 2.4 7.5 221.5 20 2930 N/A N/A N/A N/A N/A N/A Target not aligned with TCC correctly.
15444 Al 30 0.6 2.4 5.8 221.5 20 2930 N/A N/A N/A N/A N/A N/A 150-micron fidu: bottom corner of target.2-mm Hex
15445 Al 30 0.6 2.4 6.3 221.5 50 2890 N/A N/A N/A N/A N/A N/A 6.5-mm x 6.5-mm from target center
15446 Al 30 0.6 2.4 5.6 221.5 50 2890 N/A N/A N/A N/A N/A N/A
1/30/2003
15448 NiAl B2 5 2.4 5.7 221.5 50 2890 N/A N/A N/A N/A N/A N/A Fresnel zone plate installed
15449 NiAl B2 5 2.4 7.7 221.5 20 2964 N/A N/A N/A N/A N/A N/A
15450 NiAl B2 5 2.4 37.0 221.5 20 2964 N/A N/A N/A N/A N/A N/A one side of sample flew out
15451 Ta 55 0.6 2.4 119.0 221.5 20 2925? N/A N/A N/A N/A N/A N/A 2-mm Hex: LLNL test expt "RICE"
15452 Al/LiF 29/2000 0.6 2.4 2.0 221.5 20 2925 N/A N/A N/A N/A N/A N/A
15453 Ta 55 0.6 2.4 215.0 221.5 50 2895 N/A N/A N/A N/A N/A N/A LLNL test expt "RICE"
15454 Al 30 0.6 1 161.0 221.5 50 2895 N/A N/A N/A N/A N/A N/A LLNL test expt "RICE"